Oxygen content and thermodynamic stability of YBaCo4O7 ± δ

Abstract

Abstract YBaCo4O7 ± δ was found to be thermodynamically stable in air at T > 900 °C whereas its thermodynamic stability at 950 °C is limited by the range of oxygen partial pressures - 5.05 ≤ log(pO2/atm) ≤ - 0.5. Oxygen content in YBaCo4O7 ± δ at 950 °C slightly decreases from 7.009 at log(pO2/atm) = - 0.5 to 6.953 in the atmosphere with log(pO2/atm) = - 5.05. YBaCo4O7 ± δ decomposes into the mixture of YCoO3-δ, BaCoO3-δ and Co3O4 at 950 °C in atmosphere with log(pO2/atm) > - 0.5 whereas in atmosphere with log(pO2/atm) < - 5.05 Y2BaCoO5, BaCoO2 and CoO were identified as the products of YBaCo4O7 ± δ decomposition. © 2015 Elsevier B.V.
No file

Dates and versions

hal-02184096 , version 1 (15-07-2019)

Identifiers

Cite

D.S. Tsvetkov, Valérie Pralong, N.S. Tsvetkova, A.Y. Zuev. Oxygen content and thermodynamic stability of YBaCo4O7 ± δ. Solid State Ionics, 2015, 278, pp.1-4. ⟨10.1016/j.ssi.2015.05.004⟩. ⟨hal-02184096⟩
20 View
0 Download

Altmetric

Share

Gmail Mastodon Facebook X LinkedIn More