CuFe2S3 as electrode material for Li-ion batteries

Abstract

Electrochemical performances of the isocubanite CuFe2S3 tested as electrode material for Li-ion batteries have been investigated. A first discharge capacity of 860 mA h g(-1) shows a conversion process leading to Li2S, copper and iron nanoparticles. Interestingly, a reversible capacity of 560 mA h g(-1) at 1.5 V is demonstrated with good cyclability up to 30 cycles.

Domains

Materials
Fichier principal
Vignette du fichier
c8ra03840f.pdf; (682.69 Ko) Télécharger le fichier
Origin : Publisher files allowed on an open archive

Dates and versions

hal-02174384 , version 1 (05-07-2019)

Licence

Attribution

Identifiers

Cite

Emmanuel Anger, Antoine Maignan, Tristan Barbier, Valérie Pralong. CuFe2S3 as electrode material for Li-ion batteries. RSC Advances, 2018, 8 (47), pp.26691-26695. ⟨10.1039/c8ra03840f⟩. ⟨hal-02174384⟩
32 View
40 Download

Altmetric

Share

Gmail Facebook X LinkedIn More