Fluoride etching opens the structure and strengthens the active sites of the layered ZSM-5 zeolite

Résumé

The NH4F etching is a chemical approach for the preparation of hierarchical zeolites without substantial modification of their framework composition and acidic properties. We employed this approach to modify the 2-dimensional form of ZSM-5 and obtain a catalyst for bulky molecules conversion. The etching conditions were varied in order to obtain hierarchical ZSM-5 with different level of dissolution. Thus, obtained derivatives of 2-dimensional ZSM-5 were thoroughly studied in order to get deep insights into the effect of fluoride treatment. The 2-dimensional ZSM-5 was found unexpectedly stable under etching conditions, which is a consequence of the high quality of zeolite crystals containing a limited number of defect zones and misoriented crystalline domains, in contrast to conventional ZSM-5. Fluoride etching was also used to de-pillar 2-dimensional ZSM-5. The morphology and textural properties of the de-pillared ZSM-5 were very similar to those of the parent layered ZSM-5. Accordingly, amorphous and extra-framework species were dissolved first, resulting in the complete removal of extra-framework Al, thereby strengthening the active sites. In summary, the fluoride etching opens the structure of layered ZSM-5 and strengthens its acid sites when combined with dealumination during calcination.

Domaines

Chimie
Fichier principal
Vignette du fichier
S1387181119300915.pdf (3.69 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-02155088 , version 1 (22-10-2021)

Licence

Identifiants

Citer

Jan Přech, Krassimir Bozhilov, Jaafar El Fallah, Nicolas Barrier, Valentin Valtchev. Fluoride etching opens the structure and strengthens the active sites of the layered ZSM-5 zeolite. Microporous and Mesoporous Materials, 2019, Special Issue dedicated to the 65 birthday of Prof. Wieslaw J. Roth, 280, pp.297-305. ⟨10.1016/j.micromeso.2019.02.023⟩. ⟨hal-02155088⟩
80 Consultations
146 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More