Fast firing of 3 mol% yttria‐stabilized zirconia: On the effect of heating rate on sintering - Normandie Université Accéder directement au contenu
Article Dans Une Revue Journal of the American Ceramic Society Année : 2024

Fast firing of 3 mol% yttria‐stabilized zirconia: On the effect of heating rate on sintering

Résumé

Abstract The impact of rapid heating on sintering is currently getting a growing scientific interest. Previous results have shown that when considering 90 nm‐sized 3 mol% yttria‐stabilized zirconia (3YSZ) powder the heating rate effect on densification is not detectable, whereas it is huge when using finer powder (≈20 nm, specific surface area, SSA = 30–60 m 2 g −1 ). Herein, we investigate the fast firing of ≈40 nm 3YSZ powder (SSA = 16 m 2 g −1 ) and compare it with conventional sintering. The results show that the heating rate has a modest effect on the final density with improvements always below 2%–3% in terms of relative density. The relatively good match between fast firing and the densification behavior predicted by the master sintering curves agrees with the observed microstructural evolution, where fast‐firing provides only a modest effect on the pore size. Finally, it is shown that the heating rate does not impact the dynamics of closed pore formation.
Fichier sous embargo
Fichier sous embargo
0 5 7
Année Mois Jours
Avant la publication
vendredi 3 janvier 2025
Fichier sous embargo
vendredi 3 janvier 2025
Connectez-vous pour demander l'accès au fichier

Dates et versions

hal-04634546 , version 1 (04-07-2024)

Licence

Identifiants

Citer

Mattia Biesuz, Emanuele de Bona, Charles Manière. Fast firing of 3 mol% yttria‐stabilized zirconia: On the effect of heating rate on sintering. Journal of the American Ceramic Society, 2024, ⟨10.1111/jace.19989⟩. ⟨hal-04634546⟩
0 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Mastodon Facebook X LinkedIn More